Airless spraying: dilution amount: 0-5% (based on paint weight ratio) Nozzle diameter: 0.4mm-0.5mm Spray pressure: 20MPa-25MPa (200kg/cm2 - 250kg/cm2) * Air spraying: diluent: epoxy series diluent. Dilution amount: 10-15% (by weight of paint) Nozzle diameter: 1.5mm-2.0mm Spray pressure: 0.3MPa-0.5MPa (3kg/cm2 - 5kg/cm2) * Roller coating: diluent: epoxy series diluent Dilution amount: 5-10% (by weight of paint) * Cleaning agent: epoxy series diluent
Precautions 1. The flame retardant glass flake coating shall be stored in a dry, ventilated and cool place, and it is strictly prohibited to be exposed to rain, sun and fire. 2. The mixing of accelerator and curing agent may cause explosion hazard. Note that the accelerator and curing agent shall be stored separately. It is strictly prohibited to mix the accelerator and curing agent directly. 3. The storage period of flame retardant glass flake coating is 3 months in summer and 6 months in winter. If the products beyond the storage period do not agglomerate, they can continue to be used after the technical indicators pass the inspection.
Product features: 1. Good flame retardancy, corrosion resistance and penetration resistance; Acid resistant, alkali resistant, salt resistant, solvent resistant and other corrosive media. 2. High temperature resistance and heat shock resistance; The heat resistance of glass flake lining is 20-40 ℃ higher than that of similar resin coating. 3. The coefficient of thermal expansion is small, which can adapt to high temperature working environment and has good thermal shock resistance; The resin layer is easy to crack and fall off under the condition of thermal shock due to the relatively large extension coefficient compared with the base materials such as steel and cement, while the glass flake coating can be developed into a thermal stable layer, thus preventing the cracking and peeling of the lining. 4. Good abrasion resistance. The coating containing glass flakes is much harder than the epoxy or polyester resin layer without glass flakes, so it has high abrasion resistance. 5. The adhesive strength is high, the adhesive strength with steel plate is ≥ 2.0mpa, and the adhesive strength with concrete is ≥ 2.5mpa, so the glass flake mastic coating is not easy to crack, delaminate, delaminate or peel; Good adhesion and impact strength, resulting in good corrosion resistance. 6. High solid content, temperature resistance and chemical resistance are superior to epoxy resin coatings. 7. The construction is convenient, the operation is simple, the quality is easy, the defective parts are easy to repair, and the coating protection life is more than 8 years. 8. The coating is cured at room temperature, with fast drying speed, good construction performance, excellent physical and mechanical properties, and electrolytic performance.