Zirconium oxide, which was extracted from precious stones by a foreigner, began to appear and was later used in gas Lampshade On. Later, this material was applied to Refractory , coloring and Abrasive materials Wait. When polishing the workpiece, put the workpiece to be grinded and high-purity zirconia beads into a rotating or vibrating barrel for grinding together, so that the workpiece can be polished or deburred. Zirconia beads are also used in some equipment because of their good grinding effect, such as the grinding effect in the daily necessities industry. For example, toothpaste for daily use is mainly composed of spices, sweeteners, wetting agents, powder friction agents and other ingredients, which is very dependent on the dispenser. It is mainly used in the gao effect machine equipment for mixing, dispersing and dissolving materials such as solid articles and liquid articles. It is also used in small chemical dispensers to meet the laboratory test requirements. It is mainly used in the laboratory disperser to test whether the performance of a small amount of emulsion can meet the design requirements, so as to pave the way for mass industrial production.
This product has high degree and toughness at normal temperature, good low abrasion resistance, temperature resistance and corrosion resistance, high rigidity, non magnetic conductivity, and electrical edge. Because of its many advantages, it has been applied in various fields. Usually there are these substances below, Y-TZP grinding balls, dispersion and grinding media injector 、 globe valve Ball socket Zirconia mould , Micro Fan Axis Optical fiber Pin, optical fiber Sleeve Drawing dies and cutting tools, low grinding tools, watch cases and watchbands, light golf bats and other room temperature low grinding devices. Therefore, zirconia ceramic accessories such as zirconia balls are being used in thermal barrier coatings, catalyst carriers, refractories, textiles and other fields.
Precautions:
1. Select suitable products according to the capacity of sander, slurry viscosity and inlet and outlet clearance. In application, the sander shall be cleaned up first, and the slurry viscosity shall be measured to see if it is in accordance with the regulations. Check whether the clearance at the inlet and outlet of the sander and the speed ratio are appropriate.
2. For initial application, first grind the epoxy resin and solvent slurry with viscosity for 30 minutes. If the slurry with lower concentration is selected for pre grinding, be sure to reduce the rotating speed ratio and keep the actual operation time within 15 minutes.
3. Because of long-term milling, a small amount of products will be crushed under high-speed collision. Therefore, it is necessary to fill in the part after a period of time. During filling, the crushed materials shall be screened with stainless steel screen mesh first, and then the proportion of equal weight to crushed materials shall be added.
4. When grinding paint, it shall be cleaned with epoxy resin. If the solvent must be used, it is necessary to reduce the speed ratio, and the actual operation time should be within 10 minutes. Intermittent cleaning of "start stop" is proposed for the netting system.
5. Under the condition that the grain size of finished products will not be changed, if the grinding time of zirconia balls is to be increased, or if the grain size cannot meet the requirements within the required time, it is necessary to fill in the appropriate.