Product features ：
This product is mainly based on Waterborne resin It is composed of environment-friendly antirust pigments, and does not contain surfactant. The non-toxic and efficient antirust raw materials have strong cathodic protection effect, and can also play a passive role on the surface of steel. This product uses water as the dispersion medium, has good film performance, and can be cured by baking. Two components need to be added curing agent High hardness, excellent adhesion, corrosion resistance, long-term performance waterproof Rust prevention, and baking at about 200 ℃ without pulverization, which can be used for anti-corrosion of hot water tank. Diluted with tap water, it is safe, environmentally friendly, convenient for construction, and has stable anti-corrosion effect.
Product use:
Applicable to various towers Water supply device , drinking water tank, automobile water tank, hot water tank Heating Pipeline, buried pipeline, sewage Water pipe Anti corrosion and rust protection shall be provided for the inner walls of roads, edible oil tanks, etc.
Construction method:
Before single component is used, 10-15% tap water can be added to dilute and mix evenly before brushing spray Roll coating. Two component is to mix the water-based resin and curing agent in a certain proportion, add 10-15% tap water to dilute, and spray, brush, roll.
quality guarantee period:
5 ℃ - 35 ℃ Cool dry At least 12 months. After the original package is opened, long time contact with the air shall be avoided. After the two-component is added with curing agent, 2-3 Use up within hours, otherwise it will gradually solidify and cause waste.
User Guide:
In order to obtain a well cured paint film, please read the product description before use. After the proportion is accurate according to the instructions, use a mixer to mix evenly before construction. The curing temperature should be above 15 ℃, the relative humidity should be below 80%, the surface drying should be 2h, and the solid drying should be 12 h， After 5 days of complete curing, heating and baking at 120 ℃ for 20-30 minutes after surface drying will accelerate the curing time and improve the anti-corrosion performance of the paint. In addition, according to the specific construction situation, it can be derusted with our company's water-based rust anticorrosive paint The supporting effect is better.
Transportation:
Non flammable and explosive, safe and non-toxic.
Color:
Black, grey, brown Iron red , transparent.
matters needing attention:
1. The dust and stains on the base course shall be cleaned before construction.
2. Do not dilute it with gasoline, rosin, xylene, Tena water, etc.
3. It is difficult to construct when the humidity is ≥ 80%, and construction in rainy days is prohibited; Construction temperature ≥ 5 ℃.
4. Protect the paint film after coating to avoid contact with water or other substances before drying.
5. After construction and application, clean the appliance with clean water to facilitate the next use.
6. If the product is splashed into eyes or clothes, it should be washed with clean water immediately. In serious cases, please see a doctor as soon as possible.